410S Stainless Steel Sheet/Plate

Product Detail

PRODUCT DESCRIPTION

Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden. 410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410S is completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.

Destructive and Non-Destructive Testing

Mechanical examining like tensile, Elongation and reduction of area.
Chemical examination
Radiographic Test
Pitting Corrosion Test
Positive material recognition
Eddy Current test
Buckling & Crushing test

SS 410S Plates Processing

Hot rolled Cold rolled Cutting Forming Drilling/ Machining Grinding Polishing Testing

Stainless Steel 410S Plates Specifications:

Specifications	ASTM A240, ASME SA240
Standard	JIS, ASTM, AISI, GB, EN, DIN
Surface	2B, 2D, BA, NO.4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching
Finish	Cold rolled, Hot rolled
Width	1000-2000mm
Length	1000-6000mm
Thickness	0.40mm – 6.00mm

Grade Specifications for Stainless Steel 410S Plates

Grade	WERKSTOFF NR.	UNS
SS 410S	1.4000	S41008

Chemical Properties of SS 410S Plates

Grade	C (max)	Si (max)	Mn	Cr	Ni	P(max)	S (max)	N (max)	Other Elements
SS 410S	0.08	1.00	1.00 max	11.50–13.50	0.20-0.55	0.040	0.030	0.060	–

Mechanical Properties of SS 410S Plates

Grade	Tensile Strength (MPa) min	Elongation (% in 50mm) min	Yield Strength 0.2% Proof (MPa) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
SS 410S	444	33	290	75	65