Model |
Be |
Ni+Co |
Ni+Co+Fe |
Al |
Si |
Cu |
C17200 |
1.8-2.0 |
≥0.20 |
≤0.6 |
≤0.2 |
≤0.2 |
Remnant |
State |
Tensile Strength |
Yield Strength |
Rockwell Hardness |
4×DA |
Electrical Conductivity |
||
Mpa |
0.2%,Mpa |
B |
Elongation |
IACS,% |
|||
min% |
|||||||
TB00 |
Solid Solution Heat Treatment (A) |
410-590 |
140 |
45-85 |
20 |
– |
|
TD04 |
Hardening State(H) |
Diameter<10mm |
620-900 |
88-103 |
|||
Diameter:10-25mm |
620-860 |
88-102 |
8 |
>17 |
|||
Diameter25-75mm |
590-830 |
520 |
88-101 |
||||
State |
Tensile Strength |
Yield Strength |
Rockwell Hardness |
4×DB |
Electrical Conductivity |
||
Mpa |
0.2%,Mpa |
B |
Elongation |
||||
min% |
|||||||
TF00 |
Heat Treatment of Deposit(AT) |
1140-1380 |
1000 |
36-42 |
4 |
– |
|
TH04 |
Hardening & Deposit Heat Treatment of Settlement(HT) |
1240-1580 |
1070 |
38-44 |
2 |
>22 |