303 STAINLESS STEEL BAR

Product Detail

303 STAINLESS STEEL BAR

303 (UNS 30300) stainless steel bars were developed for machining. Type 303 has a higher concentration of sulfur reducing the drag on cutting tools. It allows greater machining speeds and lower production costs. The alloy is useful whenever a need arises for good corrosion resistance and considerable machining is required. Austenitic steels have austenite as their primary phase (face centered cubic crystal). These are alloys containing chromium and nickel (sometimes manganese and nitrogen), structured around the Type 302 composition of iron, 18% chromium, and 8% nickel. Austenitic steels are not hardenable by heat treatment. The most familiar stainless steel is probably Type 304, sometimes called T304 or simply 304. Type 304 surgical stainless steel is austenitic steel containing 18-20% chromium and 8-10% nickel. Available shapes: Hexes, Rounds, Squares

Typical Chemical Properties
Minimum Properties
Tensile Strength , psi	85,000
Yield Strength, psi	45,000
Elongation	50%
Hardness	Rb 180
Chemistry
Carbon( C)	.15 max
Chrome (Cr)	17.0- 19.0
Manganese (Mn)	2.0 max
Nickel ( Ni)	8.0 -10.0
Phosphorus (P)	0.20 max
Sulphur (S)	.15 min
Silicon (Si)	1.00 max

Stainless steel hot rolled & Anealed & Pickled angle:

Available size:

Width(mm)	Thickness (mm)
20*20	3
25*25	3	4	5
30*30	3	4	5
40*40	3	4	5	6
50*50	3	4	5	6	7
60*60	5	6	7	8
65*65	5	6	7	8
70*70	6	7	8	9	10
75*75	6	7	8	9	10
80*80	7	8	9	10
100*100	8	9	10	12

2.Stainless steel U channel

Hot rolled U channel Available sizes (mm):

Thickness			Height	Width
3	5	6	80	40
4	5	6	100	50
5	6	7	120	50
	6	7	140	60

Welded U channel Available sizes(mm):

Thickness			Height														Width
3	4	5	50	55	60	65	70	75									25
3	4	5	60	65	70	75	80										30
3	4	5	80	85	90	95	100	105	110	115	120	125	130	135	140	145	40
			150	155	160	165	170	175	180
4	5	6	100	105	110	115	120	125	135	140	145	150	155	160			50
			165	170	175	180	185	190	195	200	205	210	215	220
5	6	7	120	125	130	135	140	145	150	155	160	165	170	175	180		60
			185	190	195	200	205	210	215	220	225	230	235	240
6	7	8	140	145	150	155	160	165	170	175	180	185	190	200			70
			205	210	215	220	225	230	235	240	245	250	255	260
6	7	9	150	155	160	165	170	175	180	185	190	195	200	205	210		75
			215	220	225	230	235	240	245	250	255	260	265	270
7	8	10	160	165	170	175	180	185	190	195	200	205	210	215	220		80
			225	230	235	240	245	250	255	260	265	270	275	289
8	9	12	200	205	210	215	220	225	235	240	245	250	255	260			100
			265	270

Chemical composition

Grade	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	N	Cu	Nb
201	≤0.15	≤1.0	5.50-7.50	≤0.05	≤0.03	16.00-18.00	3.50-5.50	-	-	0.05-0.25	-	-
202	≤0.15	≤1.0	7.50-10.00	≤0.05	≤0.03	17.00-19.00	4.00-6.00	-	-	0.05-0.25	-	-
301	≤0.15	≤1.0	≤2.0	≤0.045	≤0.03	16.00-18.00	6.00-8.00	-	-	≤0.1	-	-
302	≤0.15	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	8.00-10.00	-	-	≤0.1	-	-
303	≤0.15	≤1.0	≤2.0	≤0.2	≥0.15	17.00-19.00	8.00-10.00	≤0.6	-	≤0.1	-	-
304	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	8.00-10.00	-	-	-	-	-
304L	≤0.03	≤1.0	≤2.0	≤0.035	≤0.03	18.00-20.00	8.00-10.00	-	-	-	-	-
304H	0.04-0.1	≤1.0	≤2.0	≤0.035	≤0.03	18.00-20.00	8.00-10.00	-	-	-	-	-
304N	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	18.00-20.00	8.00-10.00	-	-	0.10-0.16	-	-
304J1	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	18.00-20.00	6.00-9.00	-	-	-	1.00-3.00	-
305	≤0.12	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	10.50-13.00	-	-	-	-	-
309S	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	22.00-24.00	12.00-15.00	-	-	-	-	-
310S	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	24.00-26.00	19.00-22.00	-	-	-	-	-
316	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	16.00-18.00	10.00-14.00	2.00-3.00	-	-	-	-
316L	≤0.03	≤1.0	≤2.0	≤0.035	≤0.03	16.00-18.00	12.00-15.00	2.00-3.00	-	-	-	-
316H	≤0.1	≤1.0	≤2.0	≤0.035	≤0.03	16.00-18.00	10.00-14.00	2.00-3.00	-	-	-	-
316N	≤0.03	≤1.0	≤2.0	≤0.035	≤0.03	16.00-18.00	10.00-14.00	2.00-3.00	-	0.10-0.16	-	-
316Ti	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	16.00-19.00	11.00-14.00	2.00-3.00	≥5C	-	-	-
317L	≤0.03	≤1.0	≤2.0	≤0.035	≤0.03	18.00-20.00	11.00-15.00	3.00-4.00	-	-	-	-
321	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	9.00-12.00	-	5C-0.7	-	-	-
347	≤0.08	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	9.00-12.00	-	-	-	-	10C-1.10
347H	≤0.1	≤1.0	≤2.0	≤0.035	≤0.03	17.00-19.00	9.00-12.00	-	-	-	-	8C-1.10
2205	≤0.03	≤1.0	≤2.0	≤0.035	≤0.03	21.00-24.00	4.50-6.50	2.50-3.50	-	0.08-0.20	-	-
2507	≤0.03	≤0.8	≤1.2	≤0.035	≤0.02	24.00-26.00	6.00-8.00	3.00-5.00	-	0.24-0.32	-	-
904L	≤0.02	≤1.0	≤2.0	≤0.045	≤0.03	19.00-23.00	23.00-28.00	4.00-5.00	-	-	1.00-2.00	-
C276	≤0.02	≤0.05	≤1.0	-	-	14.00-16.50	Other	-	-	-	-	-
Monel400	≤0.3	≤0.5	≤2.0	-	≤0.024	-	≥63	-	-	-	28-34	-
409L	≤0.03	≤1.0	≤1.0	≤0.035	≤0.03	17.00-19.00	-	-	-	-	-	-
410	≤0.15	≤1.0	≤1.0	≤0.035	≤0.03	11.50-13.50	-	-	-	-	-	-
410L	≤0.03	≤1.0	≤1.0	≤0.035	≤0.03	11.50-13.50	-	-	-	-	-	-
420J1	0.16-0.25	≤1.0	≤1.0	≤0.035	≤0.03	12.00-14.00	-	-	-	-	-	-
420J2	0.26-0.40	≤1.0	≤1.0	≤0.035	≤0.03	12.00-14.00	-	-	-	-	-	-
430	≤0.12	≤1.0	≤1.0	≤0.035	≤0.03	16.00-18.00	-	-	-	-	-	-
436L	≤0.025	≤1.0	≤1.0	≤0.035	≤0.03	16.00-19.00	-	-	-	-	-	-
439	≤0.03	≤1.0	≤1.0	≤0.035	≤0.03	16.00-18.00	-	-	-	-	-	-
440A	0.60-0.75	≤1.0	≤1.0	≤0.035	≤0.03	16.00-18.00	-	≤0.75	-	-	-	-
440B	0.75-0.95	≤1.0	≤1.0	≤0.035	≤0.03	16.00-18.00	-	≤0.75	-	-	-	-
440C	0.95-1.2	≤1.0	≤1.0	≤0.035	≤0.03	16.00-18.00	-	≤0.75	-	-	-	-
441	≤0.03	0.2-0.8	≤0.7	≤0.03	≤0.015	17.50-18.50	-	≤0.5	0.1-0.5	≤0.025	-	0.3+3C-0.9