4j36 Invar Alloy Wire Low Expansion Alloy Feni36 Wire

4j36/ K93600// Invar 36/ 1.3912 Precision Alloy Wire

  INVAR 36 is a nickel-iron, low expansion alloy containing 36% nickel. It maintains nearly constant dimensions over the range of normal atmospheric temperatures, and has a low coefficient of expansion from cryogenic temperatures to about 500° F. The alloy also retains good strength and toughness at cryogenic temperatures. INVAR 36 can be hot and cold formed and machined using processes similar to austenitic stainless steels. INVAR 36 is weldable using Filler Metal CF36 which is available in bare wire for both the GTAW and GMAW process.   Ferro nickel alloy: FeNi36, FeNi36, Permalloy ((1J79, 1J86, 1J85), 4J29(Kover), 79Ni4MoFe, 80Ni5MoFe, 1J50 (Ni50)   AFNOR NF A54-301 (chemistry only) ASTM F 1684-06 EN 1.3912 UNS K93600, UNS K93603 Werkstoff 1.3912 Invar 36
GB/T UNS AISI/ASTM W.Nr
4J36 K93600 Invar36 1.3912
2.Invar 36 Chemical composition:
Alloy % Ni Cr Fe C Mn Si P S
Invar 36 Min. 35 Balance 0.2
Max. 37 0.5 0.05 0.6 0.3 0.02 0.02
Invar 36 Physical properties:
Density 8.1 g/cm3
Melting point 1430 ºC
Invar 36 Mechanical properties in the room temperature:
Alloy state Tensile strength Rm N/mm2 Yield strength RP0.2 N/mm2 Elongation A5 % Brinell hardness HB
Invar 36 490 240 42 ≤200
average coefficient of linear expansion(10-6ºC)
20~100ºC 20~300ºC 20~400ºC 20~450ºC 20~500ºC 20~530ºC 20~600ºC
-- ≤1.5 -- -- -- -- --
3.Applied field: Invar 36 suit for need to apply ultra-low coefficient of heat expansion environment.Typical applications are as follows: 1.Liquefied gas production, storage and transport 2.The measurement and control instruments work temperature lower than 200ºC, such as temperature regulating device 3.Metals and other materials use the screw connector bush 4.Bimetal and bimetallic temperature controller 5.Film framework 6.Shadow mask 7.CRP components of the aviation industry temper Die 8.lower than -200ºC the satellite and missile electronic control unit framework 9.The auxiliary tube of the electromagnetic lens in the laser control device