904L Stainless Steel bolts and UNS S08904 Hex Nuts/ Studs

ER385 (904L) is used for welding materials of similar chemical composition, which are used for fabrication of equipment and vessels for handling of sulfuric acid and many chloride containing media. This filler metal may also find applications for joining Type 317L material where improved corrosion resistance in specific media is needed. In order to reduce the propensity for fissuring and hot cracking, the low melting constituents such as carbon, silicon, and phosphorus are controlled to lower levels in this alloy.     904L is a high-alloy austenitic stainless steel with low carbon content. 904L has good resistance to general corrosion, particularly in sulfuric and phosphoric conditions. It has been application proved over many years and was originally developed to resist corrosion in dilute sulfuric acid.   904L Specification  
N08904 1.4539
  904L Chemical composition  
Grade % Ni Cr Mo Cu Fe C Mn P S
904L Min 24 19 4 1 Bal.
Max 26 21 5 2 0.02 2 0.03 0.015
  904L Mechanical properties:(Minimum value at 20°C)  
Tensile Strengthσb/MPa Yield Strengthσp0.2/MPa Elongationσ5 /%
490 215 35
  904L Standard  
Bar Forging Sheet/Strip Wire Pipe Welding wire
ASTM B649 - ASTM B625 ASTM B649 ASTM B677 ASTM B673 AWS A5.9ER385