CZ112 (CW712R)
Category：ASTM Wrought Copper Alloy
Type：Naval Brass
| Chemical Composition mass/% |
| Cu |
Sn |
Al |
Fe |
Mn |
Ni |
Pb |
Si |
P |
Zn |
| 59-62 |
0.5-1.0 |
_ |
0.1 |
_ |
_ |
0.2 |
_ |
_ |
Rem |
| Mechanical properties |
| Tensile strength Mpa(Min) |
Yield strength MPa(Min) |
Elongation % |
Brinell hardness(HB) |
| 380-600 |
170-450 |
Jun-50 |
106-200 |
Note：
1、In Chemical Composition, Single values represent maximums.
2、Mechanical performance of hardness value is only for reference
CZ112 (CW712R)
CZ112 (CW712R) is commonly referred to as naval brass due its corrosion resistance in seawater and other mildly aggressive environments. The alloy contains 62% copper and 37% zinc, with a 1% tin addition for improved corrosion resistance and a harder and stronger duplex structure to improve the mechanical properties. CZ112 (CW712R) has good strength levels combined with an excellent hot formability.
Related Specifications of CZ112 (CW712R)
- C46400
- CW712R
- BS2874
- ASTM B21
- CuZn38Sn1
- CuZn36Sn1Pb (EU)
Nominal Composition of CZ112 (CW712R)
Cu 62%, Zn 37%, Sn 1%
Mechanical Properties of CZ112 (CW712R)
| Ultimate Tensile Strength (N/mm²) |
Proof Stress (N/mm²) |
Elongation (%) |
Hardness (HB) |
| 350-400 |
|
15-20 |
|
Key Features of CZ112 (CW712R)
- Very good corrosion resistance in marine environments
- Excellent hot formability
Applications of CZ112 (CW712R)
Offshore & marine | Marine hardware, tube plates and fasteners for corrosion-resistant service
Other | High strength cold-headed products and fasteners