| Grade | C | Mn | Si | P | S | Cr | Ni | Mo | N |
| S31803 | 0.03 max | 2.0 max | 1.0 max | 0.03 max | 0.010 max | 21.0 – 23.0 | 4.5- 6.5 | 2.5 – 3.5 | 0.08 – 0.20 |
| S32205 | 0.03 max | 2.0 max | 1.0 max | 0.03 max | 0.010 max | 22.0 – 23.0 | 4.5- 6.5 | 3.0 – 3.5 | 0.14 – 0.20 |
| Tensile Strength | 650 -850MPa |
| Elongation (Min) | 30 % |
| Product | Stainless Steel Strip |
| Material Type | Ferrite stainless steel, magnetic; Austenitic stainless steel, Non-magnetic. |
| Material Origin | TISCO, BAOSTEEL, JISCO, LISCO, BAOSTEEL, DINGXIN |
| Grade | 430, 410S, 409L, 201, 304 |
| Technology | Cold Rolled |
| Thickness | 0.17mm to 2.0mm |
| Width | 10mm to 250mm |
| Surface | 2B, 2D, BA, NO.4, HL, SB |
| Edge | Slit / Trim Edge |
| Other Service | Leveling: improve flatness, esp. for items with high flatness request. |
| Skin-Pass: improve flatness, higher brightness | |
| Protection | 1. Inter paper available |
| 2. PVC protecting film available | |
| ** The sizes or thicknesses of stainless steel coil can be customized. | |
| ** All standard products are supplied without inter paper & film. If needed, please inform. | |
| Finish | Thickness | Characteristics | Applications |
| No. 1 | 3.0mm~50.0mm | Finished by hot-rolling, annealing and pickling, characterized by white pickled surface | Chemical industry equipment, Industrial tanks |
| No. 2B | 0.3mm~6.0mm | Finished by heat treatment, pickling after cold rolling, followed by skin pass line to be more brighter and smooth surface | General Application Medical Instruments, Tableware |
| No. BA (Bright Annealed) | 0.5mm~2.0mm | Bright heat treatment after cold rolling | Kitchen utensil, kitchen ware, architectural purpose |
| No. 4 | 0.4mm~3.0mm | Polishing with No. 150 to No.180 mesh abrasives. The most popular finishes | Milk & Food processing facilities, Hospital Equipment, Bath-tub |
| No. 8 | 0.5mm~2.0mm | A mirror-like reflective surface by polishing with finer abrasives over 800 mesh | Reflector, Mirror, Interior-Exterior decoration forbuilding |
| HL(Hair Line) | 0.4mm~3.0mm | Finished by continuous linear polishing | Architectural purposes, escalators, kitchen ware vehicles |
|
Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Ti |
N |
Cu |
Nb |
|
201 |
≤0.15 |
≤1.0 |
5.50-7.50 |
≤0.05 |
≤0.03 |
16.00-18.00 |
3.50-5.50 |
- |
- |
0.05-0.25 |
- |
- |
|
202 |
≤0.15 |
≤1.0 |
7.50-10.00 |
≤0.05 |
≤0.03 |
17.00-19.00 |
4.00-6.00 |
- |
- |
0.05-0.25 |
- |
- |
|
301 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
16.00-18.00 |
6.00-8.00 |
- |
- |
≤0.1 |
- |
- |
|
302 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
8.00-10.00 |
- |
- |
≤0.1 |
- |
- |
|
303 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.2 |
≥0.15 |
17.00-19.00 |
8.00-10.00 |
≤0.6 |
- |
≤0.1 |
- |
- |
|
304 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
|
304L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
|
304H |
0.04-0.1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
|
304N |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
0.10-0.16 |
- |
- |
|
304J1 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
6.00-9.00 |
- |
- |
- |
1.00-3.00 |
- |
|
305 |
≤0.12 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
10.50-13.00 |
- |
- |
- |
- |
- |
|
309S |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
22.00-24.00 |
12.00-15.00 |
- |
- |
- |
- |
- |
|
310S |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
24.00-26.00 |
19.00-22.00 |
- |
- |
- |
- |
- |
|
316 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
- |
- |
- |
|
316L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
12.00-15.00 |
2.00-3.00 |
- |
- |
- |
- |
|
316H |
≤0.1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
- |
- |
- |
|
316N |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
0.10-0.16 |
- |
- |
|
316Ti |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-19.00 |
11.00-14.00 |
2.00-3.00 |
≥5C |
- |
- |
- |
|
317L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
11.00-15.00 |
3.00-4.00 |
- |
- |
- |
- |
|
321 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
5C-0.7 |
- |
- |
- |
|
347 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
- |
- |
- |
10C-1.10 |
|
347H |
≤0.1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
- |
- |
- |
8C-1.10 |
|
2205 |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
21.00-24.00 |
4.50-6.50 |
2.50-3.50 |
- |
0.08-0.20 |
- |
- |
|
2507 |
≤0.03 |
≤0.8 |
≤1.2 |
≤0.035 |
≤0.02 |
24.00-26.00 |
6.00-8.00 |
3.00-5.00 |
- |
0.24-0.32 |
- |
- |
|
904L |
≤0.02 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
19.00-23.00 |
23.00-28.00 |
4.00-5.00 |
- |
- |
1.00-2.00 |
- |
|
C276 |
≤0.02 |
≤0.05 |
≤1.0 |
- |
- |
14.00-16.50 |
Other |
- |
- |
- |
- |
- |
|
Monel400 |
≤0.3 |
≤0.5 |
≤2.0 |
- |
≤0.024 |
- |
≥63 |
- |
- |
- |
28-34 |
- |
|
409L |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
- |
- |
- |
- |
- |
- |
|
410 |
≤0.15 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
11.50-13.50 |
- |
- |
- |
- |
- |
- |
|
410L |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
11.50-13.50 |
- |
- |
- |
- |
- |
- |
|
420J1 |
0.16-0.25 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
12.00-14.00 |
- |
- |
- |
- |
- |
- |
|
420J2 |
0.26-0.40 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
12.00-14.00 |
- |
- |
- |
- |
- |
- |
|
430 |
≤0.12 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
- |
- |
- |
- |
- |
|
436L |
≤0.025 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-19.00 |
- |
- |
- |
- |
- |
- |
|
439 |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
- |
- |
- |
- |
- |
|
440A |
0.60-0.75 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
|
440B |
0.75-0.95 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
|
440C |
0.95-1.2 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
|
441 |
≤0.03 |
0.2-0.8 |
≤0.7 |
≤0.03 |
≤0.015 |
17.50-18.50 |
- |
≤0.5 |
0.1-0.5 |
≤0.025 |
- |
0.3+3C-0.9 |