One of Hottest for Stainless Steel Plate 304 - TISCO/POSCO/BAOSTEEL 430 stainless steel plate – Cepheus

   PRODUCT DESCRIPTION These sheets are hot and cold drawn for advance rolling techniques. Sheets refined through the heat treatment process to get proper sheet structure. Additionally polished with bright black polish and finished via 2B, NO3 finish NO4 finish, BA finish, and hairline and sandblasting. Sheets are manufactured in different specifications, grades, and thickness to meet the expectations of customers.   AISI/SS 430 Sheet characteristics: Heat and corrosion resistance 75% ductility Stretcher strains as chromium grades Roping with the result of stretching Weldable with non-rigorous materials Magnetic in all conditions Good annealed condition Sturdy finish Resistance to pitting and stress cracking   Under various testing defected product can be removed, only finest product deliver to the clients. Following are the tests performed Chemical test/spectro test Ultrasonic test Destructive/ non-destructive test Positive material test Intergranular corrosion test Raw material test Flattening/ flaring test Mechanical test/ tensile test Visual inspection test Third party inspection test  

Stainless Steel 430 Sheets Specifications:

Specifications ASTM A240, ASME SA240
Dimensions ASTM, ASME and API
Standard JIS, AISI, ASTM, GB, DIN, EN, etc.
Surface 2B  BA  HL  NO.3  NO.4  8K
Width 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm,etc.
Finish Black,Bright Polished,Rough Turned,No.4 Finish,Matt Finish,BA Finish
Length 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc.

Grade Specifications for Stainless Steel 430 Sheets

Grade WERKSTOFF NR. AISI UNS AFNOR BS IS JIS SIS UNI
SS 430 1.4016 430 S43000 Z 8 C 17 430 S 17 X10 Cr 17 SUS 430 142320 X12Cr17C
 

Chemical Properties of SS 430 Sheets

Grade Cr Mn Si C P S Fe
SS 430 16.00 – 18.00 0.0 – 1.00 0.0 – 1.00 0.0 – 0.08 0.0 – 0.04 0.0 – 0.02 Balance

  • One of Hottest for Stainless Steel Plate 304 - TISCO/POSCO/BAOSTEEL 430 stainless steel plate – Cepheus Related Video: