2017 Latest Design Stainless Steel Strip 304 - 6063 aluminum coil – Cepheus

Alloy : 6063 Thickness : 0.15-6.0mm Temper: All available, H1X, H2X, H3X, O, HXXX Width : 25-1600mm Coil ID: 75mm, 150mm, 200mm, 300mm, 400mm, 508mm or negotiable Production process: cold rolled, hot rolled

6063 aluminum coil

CATEGORY AND TAGS: Aluminum Coil , ,
Alloy : 6063 Thickness : 0.15-6.0mm Temper: All available, H1X, H2X, H3X, O, HXXX Width : 25-1600mm Coil ID: 75mm, 150mm, 200mm, 300mm, 400mm, 508mm or negotiable
enquiry
    • Specifications
6063 Aluminum coil is an aluminium alloy with magnesium and silicon as the alloying elements, with moderate strength, good corrosion resistance, weldability, oxidation effect. The mechanical properties of 6063 depend greatly on the temper, or heat treatment, of the material. Commonly used tempers are O, T4, T6, T651, F etc. Haomei 6063 aluminium alloy coil has JIS, AISI, ASTM, GB, DIN, EN certificates. Alloy : 6063 Thickness : 0.15-6.0mm Temper: All available, H1X, H2X, H3X, O, HXXX Width : 25-1600mm Coil ID: 75mm, 150mm, 200mm, 300mm, 400mm, 508mm or negotiable Production process: cold rolled, hot rolled  

Chemical Composition of 6063 Aluminium Coil

 
Grade Si Fe Cu Mn Mg Cr Ni Zn Al
6063 0.20-0.6 0.350 0.100 0.100 0.45-0.9 0.100 0.100 remains
6063 aluminum coil has generally good mechanical properties and is heat treatable and highly wieldable. The material can be re-heat-treated to restore a higher temper for the whole piece. 6063 al coil is typically produced with very smooth surfaces fit for anodizing and widely used in the requirements of a certain strength and high resistance to antibacterial corrosion of various industrial structural parts, such as auto parts, architectural fabrication, window and door frames, aluminium furniture, electronic components as well as various consumer durable products.

Temper of 6063 Aluminum Coil

F Processing state
H Strain hardening state
O Annealing
T Heat treatment state
H112 Pure state of strain hardening,adjustment has been made to degree of strain hardening and annealing
T4 Solid solution treatment and natural efficiency to achieve sufficient stability condition
T5 Artificial aging condition of the reentry after high temperature thermal cooling
T6 Artificial aging state after solid solution treatment