High temperature alloy soft bright Cr20Ni30 wire heat resistant for oven

High temperature alloy soft bright Cr20Ni30 wire heat resistant for oven
Nickel-chromium, nickel, ferrochrome alloy wire with electric high temperature oxidation resistance, high strength, not soften and a series of advantages. When used in a long time, the same type and the permanent elongation is very small, which is more Cr20Ni80 alloy with excellent comprehensive properties, is to produce high-quality varieties of choice for electric components.
Performance material
Cr10Ni90
Cr20Ni80
Cr30Ni70
Cr15Ni60
Cr20Ni35
Cr20Ni30
Composition
Ni
90
Rest
Rest
55.0~61.0
34.0~37.0
30.0~34.0
Cr
10
20.0~23.0
28.0~31.0
15.0~18.0
18.0~21.0
18.0~21.0
Fe
≤1.0
≤1.0
Rest
Rest
Rest
Maximum temperature℃
1300
1200
1250
1150
1100
1100
Meltiing point ℃
1400
1400
1380
1390
1390
1390
Density g/cm3
8.7
8.4
8.1
8.2
7.9
7.9
Resistivity  at 20℃((μΩ·m)
1.09±0.05
1.18±0.05
1.12±0.05
1.00±0.05
1.04±0.05
Elongation at rupture
≥20
≥20
≥20
≥20
≥20
≥20
Specific heat
J/g.℃
0.44
0.461
0.494
0.5
0.5
Thermal conductivity
KJ/m.h℃
60.3
45.2
45.2
43.8
43.8
Coefficient of lines expansion
a×10-6/
(20~1000℃)
18
17
17
19
19
Micrographic structure
Austenite
Austenite
Austenite
Austenite
Austenite
Magnetic properties
Non-magnetic
Non-magnetic
Non-magnetic
Weak magnetic
Weak magnetic
Related Products

product recommendation

Inconel Alloy 600 Wire

Inconel X750 spring temper wire

9999 pure silver wire

pure copper wire

pure copper flat bus bar

Thermocouple Compensation Wire

OEM SERVICE
Certifications
 
Cr20Ni80, Cr30Ni70, Cr15Ni60, Cr20Ni35, Cr20Ni30   
Alloy Nomenclature Performance Cr20Ni80 Cr30Ni70 Cr15Ni60 Cr20Ni35 Cr20Ni30
Main Chemical composition Ni Rest Rest 55.0-61.0 34.0-37.0 30.0-34.0
Cr 20.0-23.0 28.0-31.0 15.0-18.0 18.0-21.0 18.0-21.0
Fe ≤1.0 ≤1.0 Rest Rest Rest
Max. continuous service temp. of element(ºC) 1200 1250 1150 1100 1100
Meltiing point ℃ 1400 1380 1390 1390 1390
Resistivity at 20ºC (μΩ·m) 1.09±0.05 1.18±0.05 1.12±0.05 1.00±0.05 1.04±0.05
Density(g/cm3) 8.4 8.1 8.2 7.9 7.9
Thermal conductivity (KJ/m·h·ºC) 60.3 45.2 45.2 43.8 43.8
Coefficient of lines expansion(α×10-6/ºC) 18 17 17 19 19
Melting point approx.( ºC) 1400 1380 1390 1390 1390
Elongation at rupture(%) >20 >20 >20 >20 >20
Micrographic structure Austenite Austenite Austenite Austenite Austenite
Magnetic properties Nonmagnetic Nonmagnetic Nonmagnetic Weak magnetic Weak magnetic