Нержавеющий лист 08Х13 / AISI 409

Нержавеющий лист 08Х13 / AISI 409

Марка
08Х13 / AISI 409
Толщина, мм.
0,3 – 4,0
Ширина, мм.
300 – 1300
Длина, мм.
300-4000
ГОСТ
5582-75
Поверхность
матовая / матовая (2В) / зеркальная (ВА) / шлифованная (4N)
Состояние поставки
мягкая / полунагартованная / нагартованная / высоконагартованная / свервысоконагартованная
  About 409L stainelss steel 409L stainless steel for corrosion, high temperature and resistance to fatigue, and can achieve longevity and lightweight exhaust system components. 409L high temperature resistance, and can achieve high efficiency of the engine and exhaust system, and to reduce the thickness of the exhaust system, can reduce exhaust emissions. 409L low cost, flexibility, and finished product rate, easy to replace, are environmentally friendly new products. Chemical composition for 409L stainless steel  
Grade C(%) Si(%) Mn(%) P(%) S(%) Cr(%) Ni(%) Ti(%) Cu(%)
409L ≤0.03 ≤1.0 ≤1.0 ≤0.04 ≤0.03 10.5-11.75 ≤0.06 6xC%-0.75 ---
      Mechanical property for 409L stainless steel
Grade tensile strengthMpa Yield StrengthMpa Elongation(%) rate of reduction in area(%) Density(g/cm3)
409L ≥360 ≥175 ≥25 --- 7.75
    Specifications for 409L stainless steel
Technical thickness Width finish Origin
Cold rolled 0.5mm-3.0mm Standard width in China:1000mmm 1219mmSpecial:can be ordered 2D TISCO / Baosteel etc
    Applications for 409L stainless steel 409L stainless steel is one of the most widely used chromium nickel stainless steel, which has good corrosion resistance, heat resistance, low temperature strength and mechanical properties. Widely used in chemical, food, medicine, paper, petroleum, atomic energy and other industries, as well as construction, kitchen utensils, tableware, vehicles, household appliances all kinds of parts. Corrosion in the atmosphere, if it is an industrial atmosphere or heavily polluted areas, it is necessary to clean in time to avoid corrosion.     Standards for 409L stainless steel GB:  00Cr11Ti(Standards from China) ASTM: 409L  (Standards from USA) DIN:  1.4512 (Standards from Europe) JIS:  SUH409L (Standards from Japan)     The weight calculation method for 409L stainless steel Weight(KG/PC)=thickness(mm) x width(Meter) x length(Meter) x 7.75     Small knowledge for 409L stainless steel Crystallization characteristicsfor 409L material The solid liquid phase region of 409L steel is very small, less than 30. Almost no gamma phase at high temperature. So 409L began to crystallize in the steel after pouring, due to direct contact with the mold surface, the degree of supercooling of liquid phase, and mold surface and promote heterogeneous nucleation, therefore, liquid phase nucleation rate is very high, the formation of surface fine equiaxed grains. The formation of fine equiaxed grains on the surface of the titanium alloy is very fast, and the titanium carbide is too short to precipitate. After the formation of the equiaxed zone, the columnar crystals are formed in the steel, but there is no columnar crystal in 409L steel. Carbon content of 409L steel is very low, even if the delta phase, the amount is very small. Therefore, the performance will not have a big impact. 409L steel has almost no alpha to gamma phase transition from high temperature to low temperature, so it is easy to grow grain, appear coarse ferrite, low strength, in continuous casting slab, cut off the line, easy to appear elbow phenomenon, affecting the normal production.