Нержавеющий лист 12Х18Н9 / AISI 304

Нержавеющий лист 12Х18Н9 / AISI 304

 
Марка
12Х18Н9 / AISI 304
Толщина, мм.
0,3 – 4,0
Ширина, мм.
300 – 1300
Длина, мм.
300-4000
ГОСТ
5582-75
Поверхность
матовая / матовая (2В) / зеркальная (ВА) / шлифованная (4N)
Состояние поставки
мягкая / полунагартованная / нагартованная / высоконагартованная / свервысоконагартованная
304/ 304L/ 304H stainless steel coil About 304/304L/304H stainless steel 304L has lower carbon content and better corrosion resistance. But 304 of the strength is higher than 304L, so 304 has a higher strength than 304L, and 304H has the best strength, because the carbon content is the highest among the three. From the application: 304 can be widely used in various departments, various fields. 304L is mainly used in welding and other fields. 304H is mainly used in high temperature resistance, corrosion resistance and other fields, also used in fields such as welding, bending, and cold deformation ability is very good, has a very high stability and enduring strength, can work in the high temperature of 650 degrees Fahrenheit About 304 material:304 stainless steel is a common stainless steel material, the density of 7.93 g/cm3, the industry is also called 18/8 stainless steel. High temperature resistance of 800 degrees, with good processing performance, high toughness characteristics, widely used in industrial and furniture decoration industry and food industry. About 304L material:304L steel as a low C in the general state, its corrosion resistance and 304 similar, but after welding or stress after its excellent corrosion resistance to the grain boundary. In the case without heat treatment, can remain good corrosion resistance, generally use 400 or less (non-magnetic, temperature -196 degrees Celsius to 800 degrees Celsius). Widely used to produce good overall performance requirements (corrosion resistance and formability) of equipment and parts. About 304H material: 304H is a kind of stainless steel, with good bending, welding process performance, corrosion resistance, high durability and organizational stability, cold deformation ability is very good. The highest temperature can reach 650 DEG C, and the oxidation resistance is up to 850 DEG C   The differences of Chemical composition for 304 304L 304H

Grade

C

(%)

Si

(%)

Mn

(%)

P

(%)

S

(%)

Cr

(%)

Ni

(%)

N

(%)

304

≤0.08

≤0.75

≤2.0

≤0.045

≤0.03

18.0-20.0

8.0-10.5

≤0.1

304L

≤0.03

≤0.75

≤2.0

≤0.045

≤0.03

18.0-20.0

8.0-12.0

≤0.1

304H

0.04-1.0

≤0.75

≤2.0

≤0.045

≤0.03

18.0-20.0

8.0-10.5

----

The differences of Mechanical property for 304 304L 304H

Grade

tensile strength

(Mpa)

Yield Strength

(Mpa)

Elongation

(%)

Hardness

(HR)

304

≥515

≥205

≥40

≥92

304L

≥485

≥170

≥40

≥92

304H

≥515

≥205

≥40

≥92

  Specifications for 304 304L 304H stainless steel

Technical

Thickness

Width

Finish

Origin

Cold rolled

0.5mm-6.0mm

Standard size in China:1000mm 1219mm 1500mm.

Special width:Can be order

2B / No.4 /HL / BA / Mirror etc

TISCO / ZPSS / JISCO / Baosteel etc

Hot rolled

3.0mm-80.0mm

Standard width in China: 1219mm 1500mm 180mm 2000mm

Special width:can be ordered

No.1

TISCO / ZPSS / Baosteel / JISCO etc

  Applications for 304 304L 304H stainless steel Overall, 304 304L 304H application is quite extensive. Mainly used in construction, decoration and other fields. 1) Because 304 with good processing properties, high toughness characteristics, widely used in industrial and furniture industry and the medical industry food etc filed.What’s more 304 stainless is Suitable for food processing, storage and transportation,Plate type heat exchange, corrugated pipe, household appliances (1, 2 kinds of tableware, kitchen cabinet, indoor pipeline, water heater, boiler, bath), auto parts (windshield wiper, muffler, mold), medical appliances, building materials, chemical, food industry, agriculture, marine parts etc..304 stainless steel is a nationally recognized food grade stainless steel. 2) But 304L with lower carbon content,so 304L is widely used in welding filed. 3) 304H has good bending, welding process performance, corrosion resistance, high durability and organizational stability, cold deformation ability is very good. The highest temperature can reach 650 DEG C, and the oxidation resistance is up to 850 DEG C.   Standards for 304 304L 304H stainelss steel

Grade

GB/T 1220-2007

ASTM

DIN

JIS

KS

304

06Cr19Ni10

304

1.4301

SUS304

STS304

304L

022Cr19Ni10

304L

1.4306

SUS304L

STS304L

304H

----

304H

----

SUS304H

STS304H

  The weight calculation method for 304 304L 304H stainless steel Weight(KG/PC)=thickness(mm) x width(Meter) x length(Meter) x 7.93   Small knowledge for 304 stainless steel steel For 304 stainless steel, the composition of the Ni element is very important, directly determine the corrosion resistance of the 304 stainless steel and its value. The most important elements of 304 material are Ni, Cr, but not limited to these two elements,specific requirements by product standards. Industry common judgment that as long as the content of Ni is greater than 8%, Cr content of more than 18%, it can be considered to be the 304 stainless steel.This is why the industry will be called stainless steel 18/8 stainless steel reasons. In fact, the relevant product standards for 304 have very clear requirements, and these products for different shapes of stainless steel standards and some differences. Here are some common product standards and testing. To determine whether a material is 304 stainless steel, must meet the requirements of each element of the product standard, as long as there is a non conformity, it can not be called the 304 stainless steel.