About 410S stainelss steel
410S belongs to martensitic stainless steel. 410S is one of the lowest content of Cr in ferritic stainless steel, it has the property of stainless steel, and the corrosion resistance is better than that of 410 420 420J1 420J2 martensitic stainless steel with high carbon content.
It has good plasticity, toughness and cold formability, and is superior to other ferritic stainless steel with higher Cr content. When the C content of 410S stainless steel is very low, the plasticity and toughness of the stainless steel can be significantly improved.
So 410S stainless steel is mainly used in the manufacture of water vapor, ammonium bicarbonate solution, parts and equipment of the oil sulfur corrosion heat lining etc..
Chemical composition for 410S stainelss steel
| Grade |
C(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
| 410S |
≤0.08 |
≤1.0 |
≤1.0 |
≤0.04 |
≤0.03 |
11.5-13.5 |
≤0.6 |
Mechanical property for 410S stainless steel
| Grade |
tensile strength
Mpa |
Yield Strength
Mpa |
Elongation
(%) |
rate of reduction in area
(%) |
Density
(g/cm3) |
| 410S |
≥490 |
≥345 |
≥24 |
≥60 |
7.75 |
Specifications for 410S stainless steel
| Technical |
Thickness |
Width |
finish |
Origin |
| Cold rolled |
0.3mm-5.0mm |
Standard width in China:1000mm 1219mm
Special width:can be ordered |
2B / BA / No/4 / HL / Mirror etc |
TISCO / Baosteel etc |
Applications for 410S stainless steel
410S is to improve the corrosion resistance of the steel and formability of steel, mainly used in the manufacture of water vapor, ammonium bicarbonate solution, parts and equipment of the oil sulfur corrosion heat lining etc..
Standards for 410S stainless steel
GB: 06Cr13 (Standards from China)
ASTM: 410S (Standards from USA)
DIN: 1.4000 (Standards from Europe)
JIS: SUS410S (Standards from Japan)
The weight calculation method for 410S stainless steel
Weight(KG/PC)=thickness(mm) x width(Meter) x length(Meter) x 7.75